新闻资讯
News Center
不锈钢材料性能--316L（1）
发布时间：
2024-03-11
| 1.常用标准 | |||||||||||||
| 标准 | 名称 | 牌号 | |||||||||||
| NB/T 47010 | 承压设备用不锈钢和耐热钢锻件 | S31603(022Cr17Ni12Mo2) | |||||||||||
| ASTM A182(ASME SA182) | 高温用锻制或轧制合金钢和不锈钢公称管道法兰、锻制管配件、阀门和零件 | F316L(S31603) | |||||||||||
| EN 10222-5 | 压力用钢锻件 第5部分：马氏体 奥氏体和奥氏体-铁素体不锈钢 |
1.4404 | |||||||||||
| JIS G3214 | 压力容器用不锈钢锻件 | SUS F316L | |||||||||||
| GB/T1220 | 不锈钢棒 | S31603(022Cr17Ni12Mo2 00Cr17Ni14Mo2) | |||||||||||
| GB/T20878 | 不锈钢和耐热钢 牌号及化学成分 | S31603(022Cr17Ni12Mo2 00Cr17Ni14Mo2) | |||||||||||
| ASTM A240(ASME SA240) | 压力容器和一般用途用铬及铬镍不锈钢板、薄板和钢带 | 316L(S31603) | |||||||||||
| ASTM A276(ASME SA276) | 不锈钢棒材和型材 | 316L(S31603) | |||||||||||
| EN 10088-1 | 不锈钢 第1部分：不锈钢清单 | 1.4404 | |||||||||||
| JIS G4303 | 不锈钢棒 | SUS316L | |||||||||||
| JIS G4304 | 热轧不锈钢板、薄板和带材 | SUS F316L | |||||||||||
| 2.化学成分 | |||||||||||||
| 牌号 | 标准 | 化学成分% | |||||||||||
| C 碳 | Si 硅 | Mn 锰 | P 磷 | S 硫 | Cr 铬 | Ni 镍 | Mo 钼 | Cu 铜 | Ti 钛 | Nb（Cb) 铌 | N 氮 | ||
| S31603 | NB/T 47010 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.015 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | - | - | - | - |
| F316L(S31603) | ASTM A182(ASME SA182) | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.030 | 16.0-18.0 | 10.0-15.0 | 2.00-3.00 | - | - | - | ≤0.10 |
| 1.4404 | EN 10222-5 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.015 | 16.5-18.5 | 10.0-13.0 | 2.00-2.50 | - | - | - | ≤0.10 |
| SUS F316L | JIS G3214 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.040 | ≤0.030 | 16.0-18.0 | 12.0-15.0 | 2.00-3.00 | - | - | - | - |
| S31603 | GB/T1220 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.030 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | - | - | - | - |
| S31603 | GB/T20878 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.030 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | - | - | - | - |
| 316L(S31603) | ASTM A240(ASME SA240) | ≤0.030 | ≤0.75 | ≤2.00 | ≤0.045 | ≤0.030 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | - | - | - | ≤0.10 |
| 316L(S31603) | ASTM A276(ASME SA276) | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.030 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | - | - | - | - |
| 1.4404 | EN 10088-1 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.015 | 16.5-18.5 | 10.0-13.0 | 2.00-2.50 | - | - | - | ≤0.10 |
| SUS316L | JIS G4303 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.030 | 16.0-18.0 | 12.0-15.0 | 2.00-3.00 | - | - | - | - |
| SUS F316L | JIS G4304 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.030 | 16.0-18.0 | 12.0-15.0 | 2.00-3.00 | - | - | - | - |
| 3.物理性能 | |||||||||||||
| 类别 | 数值 | 单位 | 备注 | ||||||||||
| 密度： | 7.98 | g/cm³ | 在20℃情况下 | ||||||||||
| 熔点： | 1375-1450 | ℃ | |||||||||||
| 4.锻造工艺规范 | |||||||||||||
| 预热/℃ | 始锻温度/℃ | 终锻温度/℃ | 冷却方式 | ||||||||||
| 815 | 1500-1600 | ≥930 | 空冷 |
|
|||||||||
| 5.热处理工艺 | ||||
| 固溶处理 1050-1100℃，水冷或空冷。硬度≤187HBW | ||||